Muon radiative energy loss (in 1.0E06 cm^2/g) in polyvinylidene chloride (Saran) [(C%2#H%2#Cl%2#)%n#] with Z/A = 0.49513 (f12.0,4f12.4) E (GeV) b_brem b_pair b_nucl b_total 2. 0.4913 0.2290 0.4417 1.1620 5. 0.6682 0.5616 0.4693 1.6991 10. 0.8122 0.8301 0.4570 2.0994 20. 0.9618 1.1148 0.4375 2.5140 50. 1.1610 1.5197 0.4160 3.0968 100. 1.3067 1.8007 0.4055 3.5129 200. 1.4428 2.0602 0.4003 3.9032 500. 1.6016 2.3124 0.3997 4.3138 1000. 1.7014 2.4541 0.4062 4.5617 2000. 1.7823 2.5582 0.4168 4.7572 5000. 1.8610 2.6473 0.4364 4.9448 10000. 1.9019 2.6893 0.4563 5.0474 20000. 1.9308 2.7158 0.4794 5.1261 50000. 1.9538 2.7372 0.5156 5.2066 100000. 1.9648 2.7459 0.5466 5.2573